Synthesis of an Anticorrosive Pigment by Thermal Treatment of Iron Oxides from Steel Industry Wastes

Vista sencilla de ítem
dc.coverageN.A.en-US
dc.coverageN.A.es-ES
dc.creatorColpas-Ruiz, María Angélica
dc.creatorGnecco-Molina, Camilo
dc.creatorJiménez-Rodríguez, Gabriel Antonio
dc.creatorPérez-Mendoza, José Andrés
dc.creatorHiguera-Cobos, Óscar Fabián
dc.date2019-07-01
dc.date.accessioned2024-07-05T19:11:50Z
dc.date.available2024-07-05T19:11:50Z
dc.descriptionThis work reports the obtaining of an anticorrosive pigment composed mainly of hematite (ɑ-Fe2O3) from a powder steel industry waste from rust scale of rebar steel. This residue is mainly composed of Fe2O3 (87.97 %), SiO2 (6.13 %), CaO (1.88 %), Al2O3 (1.30%) and MnO (0.77 %). The total iron oxide of the residue is constituted by the following crystalline phases: magnetite, maghemita, lepidocrocita, wüstite, goethite and hematite. The production of a pigment with a high content of hematite was possible thanks to the high content of precursor iron oxides, which were calcined at different temperatures (750-850 °C) and holding times (0.5-1.50 h). For characterizing the iron content chemically and to identify their iron oxides phases, it was used X-ray fluorescence (XRF) and X-ray diffraction (XRD). The results showed that the pigment with the highest amount of hematite (ɑ-Fe2O3) was obtained at a calcination temperature of 850 °C and a holding time of 1.00 h.en-US
dc.descriptionEste trabajo reporta la obtención de un pigmento anticorrosivo compuesto principalmente por hematita (ɑ-Fe2O3) a partir de un residuo siderúrgico en polvo proveniente de la cascarilla de óxido superficial de varillas de acero para refuerzo de concreto. Este residuo está compuesto principalmente por Fe2O3 (87.97 %), SiO2 (6.13 %), CaO (1.88 %), Al2O3 (1.30%) y MnO (0.77 %). El óxido de hierro total del residuo está constituido por las siguientes fases cristalinas: magnetita, wustita, lepidocrocita y hematita. La producción de un pigmento con alto contenido de hematita fue posible gracias al alto contenido de óxidos de hierro precursores, los cuales fueron calcinados a diferentes temperaturas (750-850 °C) y tiempos de sostenimiento (0.5-1.50 h). Para caracterizar químicamente el contenido de hierro e identificar sus fases en óxidos de hierro, se utilizaron las técnicas de fluorescencia de rayos X (XRF) y difracción de rayos X (XRD). Los resultados mostraron que el pigmento con mayor cantidad de hematita (ɑ-Fe2O3) se obtuvo a una temperatura de calcinación de 850 °C y un tiempo de sostenimiento de1.00 h.es-ES
dc.formatapplication/pdf
dc.formatapplication/pdf
dc.formatapplication/xml
dc.identifierhttps://revistas.uptc.edu.co/index.php/ingenieria/article/view/9653
dc.identifier10.19053/01211129.v28.n52.2019.9653
dc.identifier.urihttps://repositorio.uptc.edu.co/handle/001/14243
dc.languagespa
dc.languageeng
dc.language.isospaspa
dc.language.isoengspa
dc.publisherUniversidad Pedagógica y Tecnológica de Colombiaen-US
dc.relationhttps://revistas.uptc.edu.co/index.php/ingenieria/article/view/9653/8015
dc.relationhttps://revistas.uptc.edu.co/index.php/ingenieria/article/view/9653/8017
dc.relationhttps://revistas.uptc.edu.co/index.php/ingenieria/article/view/9653/8248
dc.rights.accessrightsinfo:eu-repo/semantics/openAccessspa
dc.rights.coarhttp://purl.org/coar/access_right/c_abf197spa
dc.sourceRevista Facultad de Ingeniería; Vol. 28 No. 52 (2019); 43-58en-US
dc.sourceRevista Facultad de Ingeniería; Vol. 28 Núm. 52 (2019); 43-58es-ES
dc.source2357-5328
dc.source0121-1129
dc.subjectanticorrosive pigmenten-US
dc.subjecthematiteen-US
dc.subjectiron oxidesen-US
dc.subjectsteel industry wasteen-US
dc.subjectthermal treatmenten-US
dc.subjectX ray diffractionen-US
dc.subjectdifracción de rayos Xes-ES
dc.subjecthematitaes-ES
dc.subjectóxidos de hierroes-ES
dc.subjectpigmento anticorrosivoes-ES
dc.subjectresiduo siderúrgicoes-ES
dc.subjecttratamiento térmicoes-ES
dc.titleSynthesis of an Anticorrosive Pigment by Thermal Treatment of Iron Oxides from Steel Industry Wastesen-US
dc.titleSíntesis de un pigmento anticorrosivo mediante el tratamiento térmico de los óxidos de hierro procedentes de residuos siderúrgicoses-ES
dc.typeresearchen-US
dc.typeinvestigaciónes-ES
dc.typeinfo:eu-repo/semantics/article
dc.typeinfo:eu-repo/semantics/publishedVersion
dc.type.coarhttp://purl.org/coar/resource_type/c_bdccspa
dc.type.coarhttp://purl.org/coar/resource_type/c_18cfspa
dc.type.coarversionhttp://purl.org/coar/version/c_970fb48d4fbd8a280spa
dc.type.versioninfo:eu-repo/semantics/publishedVersionspa
dspace.entity.typePublication

Archivos

Colecciones

Revista Facultad de Ingeniería